1 1 this test method covers the determination of tensile properties of plastics in the form of thin sheeting and films less than 1 0 mm 0 04 in in thickness.
Standard test method for tensile properties of thin plastic sheeting.
The number immediately following the designation indicates the year of original adoption or in the case of revision the year of last revision.
1 1 this test method covers the determination of tensile properties of plastics in the form of thin sheeting and films less than 1 0 mm 0 04 in in thickness.
A number in parentheses indicates the year of last reapproval.
These characteristics are found through a process called tensile testing.
1 1 this test method covers the determination of tensile properties of plastics in the form of thin sheeting including film less than 1 0 mm 0 04 in in thickness.
Note 1 film has been arbitrarily defined as sheeting having nominal thickness not greater than 0 25 mm 0 010 in.
Note 1 film is defined in terminology.
Materials with a thickness greater than 14 mm 0 55 in shall be reduced by machining.
Standard test method for tensile properties of thin plastic sheeting is a standard that looks to specifically dive into the delineation of characteristics in plastics relating to tension.
Note 1 film is defined in terminology d883 as an optional term for sheeting having a nominal thickness no greater than 0 25 mm 0 010 in.
Standard test method for tensile properties of thin plastic sheeting1 this standard is issued under the fixed designation d 882.
Astm d882 02 standard test method for tensile properties of thin plastic sheeting description this test method covers the determination of tensile properties of plastics in the form of thin sheeting including film.
However for testing specimens in the form of thin sheeting including film less than 1 0 mm 0 04 in in thickness astm standard d882 is the preferred test method.
Film is defined in terminology d883 as an optional term for sheeting having a nominal thickness no greater than 0 25 mm 0 010 in.